ABS-Like+
Manufacturer: Phrozen
Type: ABS-Like Resin
ABS-Like+ is a ABS-Like Resin resin manufactured by Phrozen, high-performance 3D printing solutions with focus on speed and precision. With 17.7% elongation at break, this resin is designed for applications requiring tough, impact-resistant applications. priced at approximately $36.30.
Key Properties
- Elongation at Break: 17.7% — moderate flexibility
- Viscosity: 130 mPa·s — low — easy to pour and clean
- Impact Resistance: 66.4 J/m — excellent impact toughness
Best Applications for ABS-Like+
- Tough enclosures, protective covers, and impact-resistant parts
Technical Specifications
Technical data for ABS-Like+| Resin Type | ABS-Like Resin |
|---|
| Shore Hardness | 75-80D |
|---|
| Viscosity | 130-180 mPa·s |
|---|
| Solid Density | 1.1 g/cm³ |
|---|
| Tensile Strength | 35.8 MPa |
|---|
| Young's Modulus | 2490 MPa |
|---|
| Elongation at Break | 17.7% |
|---|
| Flexural Modulus | 1900 MPa |
|---|
| Flexural Strength | 80 MPa |
|---|
| Izod Impact (Notched) | 66.4 J/m |
|---|
| Price | $36.30 |
|---|
Handling & Printing Notes
With a viscosity of 130 mPa·s, this resin pours easily and requires minimal heating. The solid density of 1.1 g/cm³ is typical for photopolymer resins. Always refer to the official technical datasheet from Phrozen for recommended print settings, exposure times, and post-curing instructions. Safety data is available in the SDS/MSDS document.
Similar Resins to Consider
About Phrozen
High-performance 3D printing solutions with focus on speed and precision. Known for large-format printers and specialty resins.
Headquarters: Hsinchu, Taiwan
View all resins from Phrozen →
Frequently Asked Questions
What is ABS-Like+ used for?
ABS-Like+ is primarily suited for tough, impact-resistant applications. making it a good choice for demanding 3D printing applications.
How much does ABS-Like+ cost?
ABS-Like+ is priced at approximately $36.30. Check Phrozen's website or authorised retailers for current pricing and availability.