High-Temperature Resin
Manufacturer: PioCreat
Type: Standard
High-Temperature Resin is a Standard resin manufactured by PioCreat. With 8% elongation at break, this resin is designed for applications requiring general-purpose 3D printing. priced at approximately —.
Key Properties
- Elongation at Break: 8% — minimal stretch — rigid
- Viscosity: 600 mPa·s — medium-high — may benefit from slight warming before use
Best Applications for High-Temperature Resin
- General-purpose SLA/MSLA 3D printing projects
- Rapid prototyping and modelling
Technical Specifications
Technical data for High-Temperature Resin| Resin Type | Standard |
|---|
| Shore Hardness | 85-89D |
|---|
| Viscosity | 600-800 mPa·s |
|---|
| Solid Density | 1.05-1.15 g/cm³ |
|---|
| Tensile Strength | 40-50 MPa |
|---|
| Young's Modulus | 800-1000 MPa |
|---|
| Elongation at Break | 8-12% |
|---|
| Flexural Modulus | 2800-3400 MPa |
|---|
| Flexural Stress at Break | 78-90 MPa |
|---|
| Price | — |
|---|
Handling & Printing Notes
With a viscosity of 600 mPa·s, this resin may benefit from slight warming before use in colder environments. The solid density of 1.05 g/cm³ is typical for photopolymer resins, resulting in lighter cured parts. Always refer to the official technical datasheet from PioCreat for recommended print settings, exposure times, and post-curing instructions.
Similar Resins to Consider
About PioCreat
Creality-group brand specializing in dental, jewelry and general 3D printing resins, with biocompatible dental materials and precision casting lines.
Headquarters: Shenzhen, China
View all resins from PioCreat →
Frequently Asked Questions
What is High-Temperature Resin used for?
High-Temperature Resin is primarily suited for general-purpose 3D printing. making it a good choice for demanding 3D printing applications.
How much does High-Temperature Resin cost?
High-Temperature Resin is priced at approximately —. Check PioCreat's website or authorised retailers for current pricing and availability.